slurry pump wear resistant rep > BD7014 slurry pump abrasion resistant paste epoxy coating

BD7014 slurry pump abrasion resistant paste epoxy coating

Slurry pump heat impact abrasion resistant paste epoxy compound coating

product description:
BD7014 slurry pump repair material is the high performance wear resistant corrosion resistant materials which compounded
by high performance abrasion resistant material and modified toughening resin.Two-components,gray paste,small particles,heat for curing.It is the upgrade product of BD7012,the wear resistant performance is
30% higher than the BD7012.Used in the repairing of mine slurry pump and other equipment of suffering from serious
erosive wear.

product features of our BD7014 slurry pump pipes high temperature wear impact resistant epoxy paste coatings:
1.With excellent performance of wear resistant and corrosion resistant
2.With very high bonding strength to metal substrates.
3.Suitable for the repairing and protecting of heavy medium erosive wear working condition

product index:

product name	physical status	operation time limit (25℃)	usable time (25℃)	range of application
BD7014 slurry pump abrasion resistant paste epoxy coatings	paste	2 hours	36 hours	Used in the repairing and pre-protecting of heavy medium erosive wear mine slurry pump,hydro-cyclones,classifier,jet machine,underflow spigot, Slurry blender and the conveying pipe elbow etc.

color	density (g/cm3)	compressive strength (kg/cm2) GB1041-79	tensile strength (kg/cm2) GB6329-86	shear strength (kg/cm2) GB7124-86	bending strength (kg/cm2) GB1042-79	relative wear resistance(steel-1) GB3960-83	working temperature （℃）
gray	2.7	1360	410	160	585	5.6	-60～125

How to use:
1.Surface treatment: Do coarsening treatment on the pending-repair area, grinding with angle grinder or sand blasting and so on, the surface after coarsening treatment should be cleaned,
the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no greasy dirt and dust.

2.Preparation: According to the weight ratio 4:1, make the A and B components mix uniformly,generally while it’s construction
and configuring adhesives (when the temperature is low,the viscosity of BD7014 is high,it’s not suitable to mix uniformly,
you should heat up the A and B components separately first,then mix them uniformly.

3.Coating: the suitable coating thickness of BD7014 is 4-20mm,make the proportioned adhesives blade coating on the metal substrates repeatedly,make the base material wet up the
substrates,then make the mixed-up material press coating on the pending-repair area repeatedly.After the coating is coated to the required size,pat it to be solid first,then blade coating towards a single
direction to make the surface be smooth,should pay attention to controlling the coating thickness during repairing,in order to
avoid appearing interference phenomenon in the assembly.

4.Curing condition:Place it for 8 hours at the temperature of 25 degree for initial curing,heat it up to the temperature of 80
degree slowly and keep this temperature for 2 hours,then heat it up to the temperature of 120 degree and keep this temperature for 2 hours.Cool it down to the room temperature slowly.

Product packaging photo of BD7014 slurry pump chemical impact corrosion wear resistant coating epoxy compound:

------分隔线----------------------------